Scotch-Weld™ 96416 DP620NS Series Urethane Adhesive, 50 mL Syringe, Viscous, Black/Milky White, 48 hr Curing

3M™ Scotch-Weld™ urethane adhesive DP620NS is a flexible, two-part polyurethane based structural adhesive that performs well in numerous applications where some flexibility is needed. It effectively bonds to many substrates such as composites, metals, wood and many plastics and rubbers, ceramics and glass (may require primer for durability). As compared to one-part sealants, 3M™ Scotch-Weld™ urethane adhesive DP620NS is fast-curing, establishes tough bonds and offers low-temperature flexibility. It dispenses as a non-sag paste for accurate and precise handling during application. This adhesive can be used for bonding dissimilar substrates, such as concrete, ceramic, wood, plastic, rubber and metal. With a 1:1 mix ratio, this urethane adhesive has a 20 min work life, reaches handing strength in 4 hr and full cure in 48 hr.

Part No.: 96416
Product Line: MMM
MFR Model: 96416
Standard/Approvals: California Pro65 Warning
Application: For transportation applications, bonding wood, metal or composite door frames to wood or other surfaces, bonding wood paneling to wood or plaster, sealing fabric water hoses, encapsulating for tamper-proofing, flexible plastic or composite bonding
Manufacturer: 3M Products
Alternate Part Number-1: 62264550302
UPC: 021200964169
Brand: Scotch-Weld™
Part Status: A
Applicable Materials: Ceramic, Glass, Hardboard, Metal, Plastic, Rubber, Wood
Composition: "30 to 60% P,P-Methylenebis(Phenyl Isocyanate), 15 to 40% 4,4-Diisocyanatodiphenylmethane Polymer, 15 to 40% Diphenylmethanediisocyanate Prepolymer, <= 1 Silane Ester Derivative, <=0.5% Carbon Black, 0.3% Chromium Compound 1, <0.1% Chromium Compound 2, <0.1% Chromium Compound 3, <0.02% Chromium (Part A)/20 to 50% Polyether Polyol, 15 to 40% Propoxylated Trimethylolpropane, 1 to 10% Amorphous Silica, 1 to 10% 1-4-Cyclohexanedimethanol, 0.1 to 5% Aluminum Oxide, 0.1 to 5% Calcium Oxide, 0.1 to 5% Isophorone Diamine, 0.1 to 5% Potassium Oxide, <= 1% Sodium Oxide, <= 0.5% m-Xylene-Alpha,Alpha-Diamine (Part B)", Application Time
Specific Gravity: 1.11 (Part A), 1 to 1.2 (Part B)
Base Type: Polyurethane
Component: 2K
Odor/Scent: Low/No Detectable (Part A), Slight Ammonia (Part B)
Color: Black (Part A), Milky White (Part B)
Container Size (mL): 50
Setting Time: 4 hr
Flash Point: 290 deg F
Container Type: Duo Pack Syringe
Form: Viscous
Series: DP620NS
Temperature Rating (deg F): 60 to 80
Type: 2-Part, Structural
Curing Time: 48 hr